GGG-60 (DIN 1693-73 ductile cast iron grade)

Description

General

GGG-60: Ferro (Fe) rest, Carbon (C) 3.40-3.80, Silicon (Si) 2.0-2.75, Manganese (Mn) 0.30-0.60, Chromium (Cr) 0.25, Molybdenum (Mo) , 1.0 (wt.%)
EN-GJS-600-3 (EN BS EN 1563 1997), 0.7060 (DIN 1693-1/2), GGG-60 (DIN 1693-1/2 ductile cast iron grade), GGG60 (DIN 1693-1/2 ductile cast iron grade), 600/3 (UK BS 2789 1995), 100.70.03 (USA ASTM A536), GS600-3 (Italy UNI 4544 1979), 4-60 (Japan JIS G 5502-1982)

Properties

Chemical properties

Minimum value Maximum value Unit Sources
%
%

Electrical properties

Minimum value Maximum value Unit Sources
kV/mm
%
V
0.45 0.75 Ohm.mm²/m

Manufacturing Properties

Minimum value Maximum value Unit Sources

Mechanical properties

Minimum value Maximum value Unit Sources
MPa
MPa
MPa
7200 7300 kg/m³
1 3 %
MPa
J/cm
MPa
550 600 MPa
MPa
340 360 MPa
170000 177000 MPa

Optical properties

Minimum value Maximum value Unit Sources

Thermal properties

Minimum value Maximum value Unit Sources
°C
1150 1250 °C
-100 350 °C
J/kg.K
25 42 W/m.K
10 13 e-6/K

Environment

1.26 mPt
0.05 Pt
485 mELU
1.55 MJ/MJ
9.45 MJ
2.59 kg
0.12 kg
Cast iron is not produced presently in the Netherlands, the production is therefore derived from the crude steel production as it was formerly. The above mentioned publication is used.Transport is added. The coal comes for 65% from Canada, 23% Australia, 12% from the EEC. Iron ore comes for 37% from Brazil, 21% Australia, 31% Europe and the remaining 11% from elsewhere. Lime is imported from Belgium. The production and emission data are for 1989. According to the current practice 50% postconsumer scrap was assumed for the final use.
Idemat 1998, Design for Sustainability, Delft University of Technology

Tags

Tags: Electrical Properties: Resistivity < 1 Ohm.mm²/m , Resistivity < 1e+10 Ohm.mm²/m , Resistivity < 1e+15 Ohm.mm²/m , Resistivity < 1e+20 Ohm.mm²/m , Maximum Resistivity ≥ 0, 01 Ohm.mm²/m , Maximum Resistivity ≥ 0, 1 Ohm.mm²/m Mechanical Properties: Density < 10.000 kg/m³ , Maximum Density ≥ 1 kg/m³ , Maximum Density ≥ 5 kg/m³ , Maximum Density ≥ 10 kg/m³ , Maximum Density ≥ 50 kg/m³ , Maximum Density ≥ 100 kg/m³ , Maximum Density ≥ 500 kg/m³ , Maximum Density ≥ 1.000 kg/m³ , Maximum Density ≥ 5.000 kg/m³ , Elongation < 5 % , Elongation < 10 % , Elongation < 50 % , Elongation < 100 % , Elongation < 500 % , Elongation < 1000 % , Maximum elongation ≥ 1 % , Tensile strength < 1.000 Mpa , Maximum tensile strength ≥ 1 Mpa , Maximum tensile strength ≥ 10 Mpa , Maximum tensile strength ≥ 100 Mpa , Yield strength < 500 Mpa , Yield strength < 1.000 Mpa , Maximum yield strength ≥ 50 Mpa , Maximum yield strength ≥ 100 Mpa , Young's modulus < 200.000 Mpa , Young's modulus < 250.000 Mpa , Young's modulus < 300.000 Mpa , Young's modulus < 350.000 Mpa , Young's modulus < 400.000 Mpa , Maximum Young's modulus ≥ 5.000 Mpa , Maximum Young's modulus ≥ 10.000 Mpa , Maximum Young's modulus ≥ 50.000 Mpa , Maximum Young's modulus ≥ 100.000 Mpa , Maximum Young's modulus ≥ 150.000 Mpa Thermal Properties: Maximum thermal expansion ≥ 10e-6K , Maximum thermal expansion ≥ 50e-6K , Maximum thermal expansion ≥ 100e-6K , Maximum melting temperature ≥ 1.000 °C , Minimum service temperature < -50 °C , Minimum service temperature < -10 °C , Minimum service temperature < 10 °C , Minimum service temperature < 50 °C , Minimum service temperature < 100 °C , Maximum service temperature > 50 °C , Maximum service temperature > 100 °C , Thermal conductivity < 100 W/m.K , Maximum thermal conductivity ≥ 0, 1 W/m.K , Maximum thermal conductivity ≥ 1 W/m.K , Maximum thermal conductivity ≥ 10 W/m.K , Thermal expansion < 50e-6/K , Thermal expansion < 100e-6/K , Maximum thermal expansion ≥ -1e-6/K , Maximum thermal expansion ≥ 1e-6/K , Maximum thermal expansion ≥ 5e-6/K , Maximum thermal expansion ≥ 10e-6/K Material Categories: Cast Iron , Ferrous Metal , Gray Cast Iron with Nodular Graphite , Metal