EN-GJS-400-15 / EN-JS1030 (CEN EN) Ductile Cast Iron

Description

Spherodial graphite iron or nodulair grey iron for casting with a minimal tensile strength of 0.4 kN/mm²

Idemat 2003

General

Main alloyant: iron/ferro (Fe) May contain some residual alloyants other than below.

Alloyant Min. Max.
Carbon (C) wt% 3.25 3.7
Silicon (Si) wt% 2.4 3
Manganese (Mn) wt% 0.1 0.3
Sulphur (S) wt% 0.005 0.02
Phosphorus (P) wt% 0.015 0.08
Magnesium (Mg) wt% 0.04 0.07
GGG40 (DIN), 0.7040 (DIN)

Properties

Chemical properties

Minimum value Maximum value Unit Sources
%
%

Electrical properties

Minimum value Maximum value Unit Sources
kV/mm
%
V
0.45 0.65 Ohm.mm²/m Idemat 2003

Manufacturing Properties

Minimum value Maximum value Unit Sources

Mechanical properties

Minimum value Maximum value Unit Sources
MPa
MPa
MPa
7100 7300 kg/m³ Idemat 2003
15 15 % Idemat 2003
MPa
J/cm
MPa
370 400 MPa Idemat 2003/CEN
MPa
250 250 MPa Idemat 2003
167000 170000 MPa Idemat 2003

Optical properties

Minimum value Maximum value Unit Sources

Thermal properties

Minimum value Maximum value Unit Sources
°C
1150 1250 °C Idemat 2003
-100 400 °C Idemat 2003
J/kg.K
25 42 W/m.K Idemat 2003
10 11.5 e-6/K Idemat 2003

Environment

1.25 mPt
0.05 Pt
485 mELU
1.47 MJ/MJ
9.45 MJ
2.59 kg
0.12 kg
Cast iron is not produced presently in the Netherlands, the production is therefore derived from the crude steel production as it was formerly. The above mentioned publication is used.Transport is added. The coal comes for 65% from Canada, 23% Australia, 12% from the EEC. Iron ore comes for 37% from Brazil, 21% Australia, 31% Europe and the remaining 11% from elsewhere. Lime is imported from Belgium. The production and emission data are for 1989. According to the current practice 50% postconsumer scrap was assumed for the final use.
Idemat 2003

Tags

Tags: Electrical Properties: Resistivity < 1 Ohm.mm²/m , Resistivity < 1e+10 Ohm.mm²/m , Resistivity < 1e+15 Ohm.mm²/m , Resistivity < 1e+20 Ohm.mm²/m , Maximum Resistivity ≥ 0, 01 Ohm.mm²/m , Maximum Resistivity ≥ 0, 1 Ohm.mm²/m Mechanical Properties: Density < 10.000 kg/m³ , Maximum Density ≥ 1 kg/m³ , Maximum Density ≥ 5 kg/m³ , Maximum Density ≥ 10 kg/m³ , Maximum Density ≥ 50 kg/m³ , Maximum Density ≥ 100 kg/m³ , Maximum Density ≥ 500 kg/m³ , Maximum Density ≥ 1.000 kg/m³ , Maximum Density ≥ 5.000 kg/m³ , Elongation < 50 % , Elongation < 100 % , Elongation < 500 % , Elongation < 1000 % , Maximum elongation ≥ 1 % , Maximum elongation ≥ 5 % , Maximum elongation ≥ 10 % , Tensile strength < 1.000 Mpa , Maximum tensile strength ≥ 1 Mpa , Maximum tensile strength ≥ 10 Mpa , Maximum tensile strength ≥ 100 Mpa , Yield strength < 500 Mpa , Yield strength < 1.000 Mpa , Maximum yield strength ≥ 50 Mpa , Maximum yield strength ≥ 100 Mpa , Young's modulus < 200.000 Mpa , Young's modulus < 250.000 Mpa , Young's modulus < 300.000 Mpa , Young's modulus < 350.000 Mpa , Young's modulus < 400.000 Mpa , Maximum Young's modulus ≥ 5.000 Mpa , Maximum Young's modulus ≥ 10.000 Mpa , Maximum Young's modulus ≥ 50.000 Mpa , Maximum Young's modulus ≥ 100.000 Mpa , Maximum Young's modulus ≥ 150.000 Mpa Material Categories: Cast Iron , Ductile Cast Iron , Ductile Iron , Ferrous Alloy , Ferrous Metal , Gray Cast Iron , Gray Cast Iron with Nodular Graphite , Grey Cast Iron , Grey Iron , Iron Alloy , Metal