Data Table for: Polymers: Engineering Polymers: POM (hom.)

Mechanical Properties

Quantity Value Unit
Young's modulus 2900 - 3500 MPa
Shear modulus 900 - 930 MPa
Tensile strength 69 - 72 MPa
Elongation 25 - 25 %
Compressive strength 31 - 31 MPa
Bending strength 50 - 80 MPa
Impact strength 0.53 - 1.2 J/cm

Physical Properties

Quantity Value Unit
Thermal expansion 81 - 104 e-6/K
Thermal conductivity 0.23 - 0.37 W/m.K
Specific heat 1465 - 1465 J/kg.K
Melting temperature 175 - 175 °C
Service temperature -60 - 110 °C
Density 1410 - 1420 kg/m3
Resistivity 1e+19 - 1e+21 Ohm.mm2/m
Breakdown potential 15 - 15 kV/mm
Dielectric loss factor 0.005 - 0.005
Friction coefficient 0.2 - 0.35
Refraction index 1.48 - 1.48
Shrinkage 1.8 - 3.2 %
Water absorption 0.25 - 0.25 %

General

     
Remarks Price recycled materal 1.15 - 1.40 EURO/ kg. POM is not or difficult to bond with an adhesive. Bonding is only possible with cyano-acrylaat after the application of a primer. With cyano-acrylaat it is not possible to bond glass, stone and concrete.
Sample

Sample: Engineering Polymers

Browse & Explore

Material category:

Search & Select

Enter search term(s)

Search

Or choose up to 3 criteria

min:  max:  min:  max:  min:  max: 
Select