Data Table for: Polymers: Engineering Polymers: PA 66

Mechanical Properties

Quantity Value Unit
Young's modulus 1700 - 2000 MPa
Shear modulus 1100 - 1200 MPa
Tensile strength 80 - 85 MPa
Elongation 12 - 300 %
Compressive strength 46 - 86 MPa
Fatigue 22 - 22 MPa
Bending strength 115 - 125 MPa
Impact strength 0.48 - 1.5 J/cm

Physical Properties

Quantity Value Unit
Thermal expansion 70 - 100 e-6/K
Thermal conductivity 0.245 - 0.27 W/m.K
Specific heat 1670 - 1670 J/kg.K
Melting temperature 260 - 260 °C
Glass temperature 78 - 78 °C
Service temperature -30 - 105 °C
Density 1130 - 1150 kg/m3
Resistivity 1e+19 - 1e+20 Ohm.mm2/m
Breakdown potential 15.2 - 18.5 kV/mm
Dielectric loss factor 0.014 - 0.04
Friction coefficient 0.25 - 0.42
Refraction index 1.53 - 1.53
Shrinkage 0.3 - 2 %
Water absorption 3 - 4 %

Environmental Data

Quantity Value Unit
Eco indicator 95 7.881 mPt
EPS 1810 mELU
Ex (in) / Ex (out) 4.11855990068281 MJ/MJ
GER 130.7 MJ
Raw materials input 91.86641 kg
Solid 0.305024 kg
Eco indicator 99 0.588 Pt
Environmental remarks Inputs and outputs for the production of 1 kg of Nylon 66 polymer in Europe. Average data for 1995.

General

     
Remarks Recycled material costs 1.28 to 1.60 Dfl/kg. Resistance against gasoline, acids and lyes.