MgAl6Zn

Category Type Material
Non-ferrous Metals Wrought Magnesium

show all types of Non-ferrous Metals

 Am100A
AM503
MgAl3Zn
MgAl6Zn
MgMn 1,5
MgZn6Zr

Data Table for: Non-ferrous Metals: Wrought Magnesium: MgAl6Zn

Mechanical Properties

Quantity Value Unit
Young's modulus 45000 - 45000 MPa
Shear modulus 17000 - 17000 MPa
Tensile strength 300 - 320 MPa
Elongation 12 - 14 %
Fatigue 140 - 140 MPa
Impact strength 0.08 - 0 J/cm
Yield strength 180 - 230 MPa

Physical Properties

Quantity Value Unit
Thermal expansion 27 - 27 e-6/K
Thermal conductivity 80 - 80 W/m.K
Specific heat 1000 - 1000 J/kg.K
Melting temperature 510 - 610 °C
Density 1800 - 1800 kg/m3
Resistivity 0.14 - 0.14 Ohm.mm2/m
Electrochemical potential -2.37 - -2.37 V

Environmental Data

Quantity Value Unit
Eco indicator 95 23.54 mPt
EPS 2970 mELU
Ex (in) / Ex (out) 8.64432597105864 MJ/MJ
GER 196 MJ
Raw materials input 22.6233566982454 kg
Solid 5.965381229 kg
Eco indicator 99 0.673 Pt
Environmental remarks 44% of the world production of magnesium comes from the US. Another 30% of the world production is won in the CIS. There are two types of technology for the refinery of magnesium: the Pidgeon process (smelting under vacuum) and the (electr.) Magnetherm process. The average energy requirement of the winning and refinery process is high. The world reycling percentage is 21%. The data is the world average for 1993.

General

     
Remarks (Mg rest, Al 6.5, Zn 1.0, Mn 0.1.5 (wt.%))