MgAl3Zn

Category Type Material
Non-ferrous Metals Wrought Magnesium

show all types of Non-ferrous Metals

 Am100A
AM503
MgAl3Zn
MgAl6Zn
MgMn 1,5
MgZn6Zr

Data Table for: Non-ferrous Metals: Wrought Magnesium: MgAl3Zn

Mechanical Properties

Quantity Value Unit
Young's modulus 45000 - 45000 MPa
Shear modulus 17000 - 17000 MPa
Tensile strength 260 - 265 MPa
Elongation 12 - 18 %
Creep strength 100 - 100 MPa
Fatigue 125 - 0 MPa
Impact strength 0.06 - 0 J/cm
Yield strength 175 - 180 MPa

Physical Properties

Quantity Value Unit
Thermal expansion 26 - 26 e-6/K
Thermal conductivity 84 - 84 W/m.K
Specific heat 1050 - 1050 J/kg.K
Melting temperature 575 - 630 °C
Density 1780 - 1780 kg/m3
Resistivity 0.1 - 0.1 Ohm.mm2/m
Electrochemical potential -2.37 - -2.37 V

Environmental Data

Quantity Value Unit
Eco indicator 95 21.96 mPt
EPS 2960 mELU
Ex (in) / Ex (out) 8.72539975399754 MJ/MJ
GER 196 MJ
Raw materials input 15.0579097338717 kg
Solid 6.0994809912 kg
Eco indicator 99 0.667 Pt
Environmental remarks 44% of the world production of magnesium comes from the US. Another 30% of the world production is won in the CIS. There are two types of technology for the refinery of magnesium: the Pidgeon process (smelting under vacuum) and the (electr.) Magnetherm process. The average energy requirement of the winning and refinery process is high. The world reycling percentage is 21%. The data is the world average for 1993.

General

     
Remarks (Mg rest, Al 3.0, Zn 1.0, Mn 0.2 (wt.%))

Sample: Wrought Magnesium