Am100A

Category Type Material
Non-ferrous Metals Wrought Magnesium

show all types of Non-ferrous Metals

 Am100A
AM503
MgAl3Zn
MgAl6Zn
MgMn 1,5
MgZn6Zr

Data Table for: Non-ferrous Metals: Wrought Magnesium: Am100A

Mechanical Properties

Quantity Value Unit
Young's modulus 45000 - 45000 MPa
Shear modulus 17000 - 17000 MPa
Tensile strength 155 - 280 MPa
Elongation 1 - 2 %
Yield strength 85 - 155 MPa

Physical Properties

Quantity Value Unit
Thermal expansion 26 - 26 e-6/K
Thermal conductivity 71 - 71 W/m.K
Specific heat 1050 - 1050 J/kg.K
Melting temperature 465 - 595 °C
Density 1810 - 1810 kg/m3
Resistivity 0.14 - 0.14 Ohm.mm2/m
Electrochemical potential -2.37 - -2.37 V

Environmental Data

Quantity Value Unit
Eco indicator 95 25.18 mPt
EPS 2450 mELU
Ex (in) / Ex (out) 8.49550898203593 MJ/MJ
GER 197 MJ
Raw materials input 29.4938805305478 kg
Solid 5.88321553571 kg
Eco indicator 99 0.682 Pt
Environmental remarks 44% of the world production of magnesium comes from the US. Another 30% of the world production is won in the CIS. There are two types of technology for the refinery of magnesium: the Pidgeon process (smelting under vacuum) and the (electr.) Magnetherm process. The average energy requirement of the winning and refinery process is high. The world reycling percentage is 21%. The data is the world average for 1993.

General

     
Remarks (Mg rest, Al 10.0, Mn >0.10 (wt.%))

Sample: Wrought Magnesium