CuZn40Pb3 (brass)

Category Type Material
Non-ferrous Metals Wrought Copper

show all types of Non-ferrous Metals

 CuAl5
CuNi10Fe
CuNi18Zn20
CuNi44Mn
CuSn6,7P0,1
CuSn8 (P bronze)
CuZn 15
CuZn 37
CuZn 40
CuZn30 (brass)
CuZn40Pb3 (brass)
E-Cu
E-CuAg

Data Table for: Non-ferrous Metals: Wrought Copper: CuZn40Pb3 (brass)

Mechanical Properties

Quantity Value Unit
Young's modulus 97500 - 97500 MPa
Shear modulus 36000 - 36000 MPa
Tensile strength 400 - 450 MPa
Elongation 20 - 30 %
Yield strength 270 - 300 MPa

Physical Properties

Quantity Value Unit
Thermal expansion 21 - 21 e-6/K
Thermal conductivity 120 - 120 W/m.K
Specific heat 376 - 376 J/kg.K
Melting temperature 875 - 890 °C
Density 8500 - 8500 kg/m3
Resistivity 0.062 - 0.062 Ohm.mm2/m

Environmental Data

Quantity Value Unit
Eco indicator 95 63.24 mPt
EPS 70100 mELU
Ex (in) / Ex (out) 24.7727272727273 MJ/MJ
GER 80.3 MJ
Raw materials input 32.3649239335742 kg
Solid 77.71925007 kg
Eco indicator 99 1.65 Pt
Environmental remarks Considerable differences appear in practice. Therefore we used the energy requirements of winning in open mines and smelting in the main producing countries US and Chile as basis. The sulfidic ore has a copper content of 0,6%. There is also a wide spread in the emission of SO2 during the refinery process. This reaches from 38 gram/kg Cu to 3500 gram/kg Cu, with an average of 1060gram / kg Cu. Often the reclaimed SO2 is used for the production of sulphuric acid. The world avererage scrap percentage is 20%.

General

     
Remarks (Cu 57.7, Zn rest, Pb 2.0-3.5 (wt.%))

Sample: Wrought Copper