Data Table for: Non-ferrous Metals: Wrought Copper: CuAl5

Mechanical Properties

Quantity Value Unit
Young's modulus 128500 - 128500 MPa
Shear modulus 47500 - 47500 MPa
Tensile strength 380 - 530 MPa
Elongation 15 - 55 %
Fatigue 160 - 160 MPa
Yield strength 150 - 450 MPa

Physical Properties

Quantity Value Unit
Thermal expansion 17 - 17 e-6/K
Thermal conductivity 80 - 80 W/m.K
Specific heat 420 - 420 J/kg.K
Melting temperature 1050 - 1080 °C
Density 8200 - 8200 kg/m3
Resistivity 0.11 - 0.11 Ohm.mm2/m

Environmental Data

Quantity Value Unit
Eco indicator 95 97.69 mPt
EPS 66700 mELU
Ex (in) / Ex (out) 38.5294117647059 MJ/MJ
GER 102 MJ
Raw materials input 15.7061239454944 kg
Solid 125.0306141856 kg
Eco indicator 99 2.45 Pt
Environmental remarks Considerable differences appear in practice. Therefore we used the energy requirements of winning in open mines and smelting in the main producing countries US and Chile as basis. The sulfidic ore has a copper content of 0,6%. There is also a wide spread in the emission of SO2 during the refinery process. This reaches from 38 gram/kg Cu to 3500 gram/kg Cu, with an average of 1060gram / kg Cu. Often the reclaimed SO2 is used for the production of sulphuric acid. The world avererage scrap percentage is 20%.

General

     
Remarks (Cu rest, Al 5.5, Ni < 0.8, Mn < 0.5 (wt.%))

Sample: Wrought Copper