GD-MgAl9Zn1

Category Type Material
Non-ferrous Metals Cast Magnesium

show all types of Non-ferrous Metals

 G-MgAl6Zn3
G-MgAl8Zn1
G-MgAl9Zn2
GD-MgAl9Zn1

Data Table for: Non-ferrous Metals: Cast Magnesium: GD-MgAl9Zn1

Mechanical Properties

Quantity Value Unit
Young's modulus 45000 - 45000 MPa
Shear modulus 17000 - 17000 MPa
Tensile strength 240 - 240 MPa
Elongation 3 - 3 %
Fatigue 120 - 120 MPa
Yield strength 160 - 160 MPa

Physical Properties

Quantity Value Unit
Thermal expansion 26 - 26 e-6/K
Thermal conductivity 68 - 68 W/m.K
Specific heat 1050 - 1050 J/kg.K
Melting temperature 468 - 595 °C
Density 1810 - 1810 kg/m3
Resistivity 0.17 - 0.17 Ohm.mm2/m
Electrochemical potential -2.37 - -2.37 V

Environmental Data

Quantity Value Unit
Eco indicator 95 24.69 mPt
EPS 2810 mELU
Ex (in) / Ex (out) 8.56280648811769 MJ/MJ
GER 197 MJ
Raw materials input 27.8113852482243 kg
Solid 5.883906938 kg
Eco indicator 99 0.678 Pt
Environmental remarks 44% of the world production of magnesium comes from the US. Another 30% of the world production is won in the CIS. There are two types of technology for the refinery of magnesium: the Pidgeon process (smelting under vacuum) and the (electr.) Magnetherm process. The average energy requirement of the winning and refinery process is high. The world reycling percentage is 21%. The data is the world average for 1993.

General

     
Remarks (Mg rest, Al 9.0, Zn 0.7, Mn >0.13 (wt.%))

Sample: Cast Magnesium