GTS-70-02

Category Type Material
Ferrous Metals Cast Iron

show all types of Ferrous Metals

 GG-15 (DIN 1961-85 steel grade)
GG-35 (DIN 1691-85 steel grade)
GGG-40 (DIN 1693-1/2 steel grade)
GGG-60 (DIN 169-73 steel grade)
GGG-70 (DIN 169-73 steel grade)
GGG-NiCr20 2
GGG-NiSiCr 20 4 2
GGL-NiCuCr15 6 2
GTS-35-10
GTS-65-02
GTS-70-02

Data Table for: Ferrous Metals: Cast Iron: GTS-70-02

Mechanical Properties

Quantity Value Unit
Young's modulus 185000 - 185000 MPa
Tensile strength 700 - 700 MPa
Elongation 2 - 2 %
Yield strength 500 - 550 MPa

Physical Properties

Quantity Value Unit
Thermal expansion 13.5 - 13.5 e-6/K
Thermal conductivity 50 - 50 W/m.K
Melting temperature 1150 - 1250 °C
Density 7400 - 7400 kg/m3
Resistivity 0.4 - 0.4 Ohm.mm2/m

Environmental Data

Quantity Value Unit
Eco indicator 95 1.282 mPt
EPS 1025 mELU
Ex (in) / Ex (out) 1.66230366492147 MJ/MJ
GER 9.93 MJ
Raw materials input 1.16672547722 kg
Solid 0.221350951450142 kg
Eco indicator 99 0.0494 Pt
Environmental remarks Cast iron is not produced presently in the Netherlands, the production is therefore derived from the crude steel production as it was formerly. The above mentioned publication is used. Transport is added. The coal comes for 65% from Canada, 23% Australia, 12% from the EEC. Iron ore comes for 37% from Brazil, 21% Australia, 31% Europe and the remaining 11% from elsewhere. Lime is imported from Belgium. The production and emission data are for 1989. According to the current practice 50% postconsumer scrap was assumed for the final use. The temper treatment is NOT included in this assessment.
Author: Idemat 1998

General

     
Remarks (Fe rest, C 2.0-2.6, Si 0.90-1.60, Mn 0.40-0.50 (wt.%))

Sample: Cast iron