GGL-NiCuCr15 6 2

Category Type Material
Ferrous Metals Cast Iron

show all types of Ferrous Metals

 GG-15
GG-35
GGG-40
GGG-60
GGG-70
GGG-NiCr20 2
GGG-NiSiCr 20 4 2
GGL-NiCuCr15 6 2
GTS-35-10
GTS-65-02
GTS-70-02

Data Table for: Ferrous Metals: Cast Iron: GGL-NiCuCr15 6 2

Mechanical Properties

Quantity Value Unit
Young's modulus 90000 - 90000 MPa
Tensile strength 140 - 170 MPa
Elongation 2 - 2 %

Physical Properties

Quantity Value Unit
Thermal expansion 18.7 - 18.7 e-6/K
Thermal conductivity 40 - 40 W/m.K
Specific heat 480 - 480 J/kg.K
Density 7400 - 7400 kg/m3
Resistivity 1.6 - 1.6 Ohm.mm2/m

Environmental Data

Quantity Value Unit
Eco indicator 95 19.56 mPt
EPS 4390 mELU
Ex (in) / Ex (out) 5.34731323722149 MJ/MJ
GER 35.1 MJ
Raw materials input 3.53815037873049 kg
Solid 0.4370473 kg
Eco indicator 99 0.349 Pt
Environmental remarks Cast iron is not produced presently in the Netherlands, the production is therefore derived from the crude steel production as it was formerly. The above mentioned publication is used. Transport is added. The coal comes for 65% from Canada, 23% Australia, 12% from the EEC. Iron ore comes for 37% from Brazil, 21% Australia, 31% Europe and the remaining 11% from elsewhere. Lime is imported from Belgium. The production and emission data are for 1989. According to the current practice 50% postconsumer scrap was assumed for the final use.
Author: Idemat 1998

General

     
Remarks (Fe rest, C <3.0, Ni 13.5-17.5, Cu 5.5-7.5, Cr 1.0-2.5, Si 1.0-2.8, Mn 1.0-1.5 (wt.%))