GG-15 (DIN)

Description

Cast Iron Alloy

General

GG-15: Ferro (Fe) rest, Carbon (C) 3.70, Silicon (Si) 2.40, Manganese (Mn) 0.50 (wt.%)
Gray Cast Iron, Grey iron, Gray iron, 20 A - 25 A (USA ASTM), FC15 (Japan JIS), GG-15 (Germany DIN), 0.6015 (Germany DIN steel number), EN-GJL-150 (DIN EN), EN-JL1020 (DIN EN steel number), 150 (UK BS), GRADE150 (UK BS), Ft 15 D (France NF), Ft150 (France AFNOR), FG15 (Spain UNE), G15 (Italy UNI)

Properties

Chemical properties

Minimum valueMaximum valueUnitSources
%
%

Electrical properties

Minimum valueMaximum valueUnitSources
kV/mm
%
V
0.81Ohm.mm²/m

Manufacturing Properties

Minimum valueMaximum valueUnitSources

Mechanical properties

Minimum valueMaximum valueUnitSources
250290MPa
MPa
MPa
70007100kg/m³
0.30.8%
7070MPa
J/cm
3000040500MPa
150250MPa
MPa
MPa
75000103000MPa

Optical properties

Minimum valueMaximum valueUnitSources

Thermal properties

Minimum valueMaximum valueUnitSources
°C
11501200°C
°C
460540J/kg.K
5050W/m.K
1013e-6/K

Environment

1.32mPt
0.1Pt
975mELU
1.34MJ/MJ
9.87MJ
2.59kg
0.12kg
Cast iron is not produced presently in the Netherlands, the production is therefore derived from the crude steel production as it was formerly. The above mentioned publication is used.Transport is added. The coal comes for 65% from Canada, 23% Australia, 12% from the EEC. Iron ore comes for 37% from Brazil, 21% Australia, 31% Europe and the remaining 11% from elsewhere. Lime is imported from Belgium. The production and emission data are for 1989. According to the current practice 50% postconsumer scrap was assumed for the final use.
Idemat 2003, Design for Sustainability, Delft University of Technology

Tags

Tags: Electrical Properties: Resistivity < 1e+10 Ohm.mm²/m , Resistivity < 1e+15 Ohm.mm²/m , Resistivity < 1e+20 Ohm.mm²/m , Maximum Resistivity ≥ 0, 01 Ohm.mm²/m , Maximum Resistivity ≥ 0, 1 Ohm.mm²/m , Maximum Resistivity ≥ 1 Ohm.mm²/m
Mechanical Properties: Bending Strength < 1.000 Mpa , Maximum Bending Strength ≥ 0, 1 MPa , Maximum Bending Strength ≥ 1 MPa , Maximum Bending Strength ≥ 10 MPa , Maximum Bending Strength ≥ 100 MPa , Density < 10.000 kg/m³ , Maximum Density ≥ 1 kg/m³ , Maximum Density ≥ 5 kg/m³ , Maximum Density ≥ 10 kg/m³ , Maximum Density ≥ 50 kg/m³ , Maximum Density ≥ 100 kg/m³ , Maximum Density ≥ 500 kg/m³ , Maximum Density ≥ 1.000 kg/m³ , Maximum Density ≥ 5.000 kg/m³ , Elongation < 1 % , Elongation < 5 % , Elongation < 10 % , Elongation < 50 % , Elongation < 100 % , Elongation < 500 % , Elongation < 1000 % , Fatigue failure < 100 Mpa , Fatigue failure < 500 Mpa , Fatigue failure < 1000 Mpa , Maximum fatigue failure ≥ 50 Mpa , Shear modulus < 50.000 MPa , Maximum shear modulus ≥ 100 Mpa , Maximum shear modulus ≥ 500 Mpa , Maximum shear modulus ≥ 1.000 Mpa , Maximum shear modulus ≥ 5.000 Mpa , Maximum shear modulus ≥ 10.000 Mpa , Tensile strength < 1.000 Mpa , Maximum tensile strength ≥ 1 Mpa , Maximum tensile strength ≥ 10 Mpa , Maximum tensile strength ≥ 100 Mpa , Young's modulus < 150.000 Mpa , Young's modulus < 200.000 Mpa , Young's modulus < 250.000 Mpa , Young's modulus < 300.000 Mpa , Young's modulus < 350.000 Mpa , Young's modulus < 400.000 Mpa , Maximum Young's modulus ≥ 5.000 Mpa , Maximum Young's modulus ≥ 10.000 Mpa , Maximum Young's modulus ≥ 50.000 Mpa , Maximum Young's modulus ≥ 100.000 Mpa
Thermal Properties: Maximum thermal expansion ≥ 10e-6K , Maximum thermal expansion ≥ 50e-6K , Maximum thermal expansion ≥ 100e-6K , Maximum melting temperature ≥ 1.000 °C , Specific heat < 1.000 J/kg.K , Specific heat < 10.000 J/kg.K , Maximum specific heat ≥ 1 J/kg.K , Maximum specific heat ≥ 10 J/kg.K , Maximum specific heat ≥ 100 J/kg.K , Thermal conductivity < 100 W/m.K , Maximum thermal conductivity ≥ 0, 1 W/m.K , Maximum thermal conductivity ≥ 1 W/m.K , Maximum thermal conductivity ≥ 10 W/m.K , Thermal expansion < 50e-6/K , Thermal expansion < 100e-6/K , Maximum thermal expansion ≥ -1e-6/K , Maximum thermal expansion ≥ 1e-6/K , Maximum thermal expansion ≥ 5e-6/K , Maximum thermal expansion ≥ 10e-6/K