Semicrystalline Ceramics:

Thermal Toughened Glass

Description

Has to be made to measure before hardening. Available in 4, 5, 6, 8, 10 and 12mm thickness.

General

Toughened glass, Tempered glass

Properties

Chemical properties

Minimum valueMaximum valueUnitSources
%
%

Electrical properties

Minimum valueMaximum valueUnitSources
kV/mm
%
V
1.00E+0181.00E+018Ohm.mm²/mIdemat 2003

Manufacturing Properties

Minimum valueMaximum valueUnitSources

Mechanical properties

Minimum valueMaximum valueUnitSources
200200MPaIdemat 2003
MPa
MPa
25002800kg/m³Idemat 2003
%
MPa
J/cm
MPa
MPa
MPa
MPa
50000100000MPaIdemat 2003

Optical properties

Minimum valueMaximum valueUnitSources

Thermal properties

Minimum valueMaximum valueUnitSources
°C
11001100°CIdemat 2003
700°CIdemat 2003
840850J/kg.KIdemat 2003
0.90.93W/m.KIdemat 2003
99e-6/KIdemat 2003

Environment

mPt
Pt
mELU
38.16MJ/MJ
MJ
kg
kg
Idemat 2003, Design for Sustainability, Delft University of Technology

Tags

Tags: Electrical Properties: Resistivity < 1e+20 Ohm.mm²/m , Maximum Resistivity ≥ 0, 01 Ohm.mm²/m , Maximum Resistivity ≥ 0, 1 Ohm.mm²/m , Maximum Resistivity ≥ 1 Ohm.mm²/m , Maximum Resistivity ≥ 1e+10 Ohm.mm²/m , Maximum Resistivity ≥ 1e+15 Ohm.mm²/m
Mechanical Properties: Bending Strength < 1.000 Mpa , Maximum Bending Strength ≥ 0, 1 MPa , Maximum Bending Strength ≥ 1 MPa , Maximum Bending Strength ≥ 10 MPa , Maximum Bending Strength ≥ 100 MPa , Density < 5.000 kg/m³ , Density < 10.000 kg/m³ , Maximum Density ≥ 1 kg/m³ , Maximum Density ≥ 5 kg/m³ , Maximum Density ≥ 10 kg/m³ , Maximum Density ≥ 50 kg/m³ , Maximum Density ≥ 100 kg/m³ , Maximum Density ≥ 500 kg/m³ , Maximum Density ≥ 1.000 kg/m³ , Young's modulus < 150.000 Mpa , Young's modulus < 200.000 Mpa , Young's modulus < 250.000 Mpa , Young's modulus < 300.000 Mpa , Young's modulus < 350.000 Mpa , Young's modulus < 400.000 Mpa , Maximum Young's modulus ≥ 5.000 Mpa , Maximum Young's modulus ≥ 10.000 Mpa , Maximum Young's modulus ≥ 50.000 Mpa , Maximum Young's modulus ≥ 100.000 Mpa
Thermal Properties: Maximum thermal expansion ≥ 10e-6K , Maximum thermal expansion ≥ 50e-6K , Maximum thermal expansion ≥ 100e-6K , Maximum melting temperature ≥ 1.000 °C , Maximum service temperature > 50 °C , Maximum service temperature > 100 °C , Maximum service temperature > 500 °C , Specific heat < 1.000 J/kg.K , Specific heat < 10.000 J/kg.K , Maximum specific heat ≥ 1 J/kg.K , Maximum specific heat ≥ 10 J/kg.K , Maximum specific heat ≥ 100 J/kg.K , Thermal conductivity < 1 W/m.K , Thermal conductivity < 10 W/m.K , Thermal conductivity < 100 W/m.K , Maximum thermal conductivity ≥ 0, 1 W/m.K , Thermal expansion < 10e-6/K , Thermal expansion < 50e-6/K , Thermal expansion < 100e-6/K , Maximum thermal expansion ≥ -1e-6/K , Maximum thermal expansion ≥ 1e-6/K , Maximum thermal expansion ≥ 5e-6/K
Material Categories: Ceramic , Ceramic Glass , Flat Glass , Glass Pane , Inorganic Compound , Non-metallic Material , Plate Glass , Safety Glass , Semicrystalline Ceramic , Sheet Glass

© 2004 - 2015 Matbase |Disclaimer